Inshine E703
Product Features
It has good cutoff function in the ultraviolet band (290-380), ensuring the anti UV ability of the component. It can convert the light in the UV band to other bands, improving the photoelectric efficiency of the component.
Product characteristics
|
Test items |
unit |
Referenced standards |
Specification value |
|
|
Wide in width |
mm |
GB/T 13542.2-2009 |
≥ standard value（0-+5） |
|
|
Weight in grams |
g/m2 |
ISO 536-2012 |
≥ standard value |
|
|
Tensile strength（MD） |
MPa |
GB/T 13542.2-2009 |
≥16 |
|
|
Tensile strength（TD） |
MPa |
GB/T 13542.2-2009 |
≥16 |
|
|
Elongation at break（MD） |
% |
GB/T 13542.2-2009 |
≥550 |
|
|
Elongation at break（TD） |
% |
GB/T 13542.2-2009 |
≥550 |
|
|
Heat shrinkage rate（120℃×3min）MD |
% |
GB/T 13542.2-2009 |
≤3.0 |
|
|
Heat shrinkage rate（120℃×3min）TD |
% |
GB/T 13542.2-2009 |
≤0.5 |
|
|
EVA and glass Peel Strength |
N/cm |
GB/T 2790-1995 |
≥80 |
|
|
EVA and cell peel strength |
N/cm |
GB/T 2790-1995 |
≥40 |
|
|
Transmittance（380-1100nm） |
% |
T/CPIA0004-2017 |
≥90 |
|
|
Transmittance（290-380nm） |
% |
T/CPIA0004-2017 |
<30 |
|
|
Volume resistivity |
Ω·cm |
GB/T 1410-2006 |
≥1×1015 |
|
|
Anti migration performance (105 ℃, 96h migration width) |
cm |
|
<0.2 |
|
|
Crosslinking degree (xylene method) |
% |
GB/T 29848-2013 |
75-95 |
|
|
Constant damp heat test 85℃×85%RH 1000H |
Yellowing index△YI |
-- |
IEC 61215-2 2016 |
≤3.0 |
|
Peel strength with glass |
N/cm |
≥40 |
||
|
UV aging resistance test 120KWH/m2 |
Yellowing index△YI |
-- |
IEC 61215-2 2016 |
≤3.0 |
|
Peel strength with glass |
N/cm |
≥40 |
||
|
PCT high temperature and high humidity experiment 48h |
Yellowing index△YI |
-- |
T/CPIA0004-2017 |
≤3.0 |
|
Peel strength with glass |
N/cm |
≥40 |
||