Inshine P601
Product Features
A highly transparent POE. With low water vapor permeability and high volume resistivity. The safety and long-term aging resistance of components operating in high temperature and humidity environments .
Product characteristics
| Test items | Unit | Referenced standards | Specification value | |
| Wide in width | mm | GB/T 13542.2-2009 | standard value（0-+5） | |
| Thickness | mm | GB/T 13542.2-2009 | 0.45-0.65 | |
| Tensile strength（MD） | MPa | GB/T 13542.2-2009 | ≥6 | |
| Tensile strength（TD） | MPa | GB/T 13542.2-2009 | ≥6 | |
| Elongation at break（MD） | % | GB/T 13542.2-2009 | ≥600 | |
| Elongation at break（TD） | % | GB/T 13542.2-2009 | ≥600 | |
| Heat shrinkage rate（120℃×3min）MD | % | GB/T 13542.2-2009 | ≤3.0 | |
| Heat shrinkage rate（120℃×3min）TD | % | GB/T 13542.2-2009 | ≤0.5 | |
| POE and backboard peel strength | N/cm | GB/T 2790-1995 | ≥60 | |
| POE and glass peel strength | N/cm | GB/T 2790-1995 | ≥80 | |
| Transmittance（380-1100nm） | % | T/CPIA0004-2017 | ≥90 | |
| Transmittance（380-290nm） | % | T/CPIA0004-2017 | ≥70 | |
| Volume resistivity | Ω·cm | GB/T 1410-2006 | ≥1×1016 | |
| Breakdown voltage intensity (AC method) | KV/mm | GB/T 1408.1-2016 | ≥28 | |
| CTI | V | GB/T 4207-2012 | ≥600 | |
| Crosslinking degree (xylene method) | % | GB/T 29848-2013 | 75-95 | |
| Surface roughness | μm | GB/T 1031-2009 | Ra（min）＞10 | |
| Haze (after crosslinking) | -- | ISO 14782:1999 | ≤5.0 | |
| Water vapor transmission rate | g/(m2·day) | GB/T 26253-2010 | ≤5.0 | |
| 38 ℃ × 90% RH | ||||
| Anti PID performance | % | IEC TS62804:2015 | ≤3% | |
| (85 ℃ × 85% RH × 192H) | ||||
| Creep performance (after crosslinking) | % | GB/T 11546.1-2008 | Creep rate ≤ 10% after 1H exposure to 0.005MPa stress in a 130 ℃ oven | |
| Constant damp heat test | Yellowing index△YI | -- | IEC 61215-2 2016 | ≤3.0 |
| 85℃×85%RH 1000H | Peel strength with glass | N/cm | ≥40 | |
| UV aging resistance test | Yellowing index△YI | -- | IEC 61215-2 2016 | ≤3.0 |
| 120KWH/m2 | Peel strength with glass | N/cm | ≥40 | |